Plastic Floor Covering WPC Composite Decking Coupling Vinyl Decking Materials

Product Details:

Place of Origin:	China
Brand Name:	Huaxiajie
Certification:	ISO9001:2000, Soncap, Intertek, SGS
Model Number:	WPC Decks40

Payment & Shipping Terms:

Minimum Order Quantity:	500 m²
Price:	Negotiate
Packaging Details:	Shrink wrap or carton for Coupling Vinyl Decking Materials
Delivery Time:	15days/20’ container, 25days/40’ container
Payment Terms:	30% TT as the deposit, the balance before delivery
Supply Ability:	900T/month

Contact Now

Detailed Product Description

Name:	Plastic Floor Covering WPC Composite Decking Coupling Vinyl Decking Materials	Material:	Coupling Vinyl With Wood
Feature:	Antiseptic / Waterproof / Anticorrosive	Color:	Dark , White Or Customized
Application:	Garden / Backyard / Swimming Pool	Size:	140mm X 25mm Or Customized
Process:	Co-extrusion, Galling, Solid

Plastic Floor Covering WPC Composite Decking Coupling Vinyl Decking Materials

Description:

Characteristic of Coupling Vinyl Decking Materials :

1	Environmental materials,recyclable
2	Saving time - light weight, easy to maintain and intall
3	Longer usage/life cycle - moistureproof
4	Durable, Stronger and more Flexible
5	Standard woodworking tools can be used
6	UV-resist and colorfast
7	Dimension stability against moisture and temperature.suitable from -40 to 60
8	Weather resistant, suitable from -40 to 60
9	Green ecological, Innovative technology, Lifestyle
10	Elegant nature wood grain texture and touch, with wood scent
11	Elegant and detailed shape design

All the standard embossing is available with this option.

It offers the best combination of price and quality.

Different surface treatment options are available as added features.

The unique embossing patterns enhance the beauty of the boards,

as well as adding to its authenticity.

Beauty/Strong/Dependable.

Specifications:

Name	Plastic Floor Covering WPC Composite Decking Coupling Vinyl Decking Materials
Size	140*25mm or customized
Length	2m, 3m, 5.9m or Customized
Color	Teak, Beech, Black Walnut, Coffee, Customized color
Material component	60% PVC+30% Wood Powder+10% special additives
Surface	Smooth, Brushed, Scratched, Grain optional
Warranty	15years
Certificate	ISO9001, ISO14001, CE, SGS
Lifetime	25years
Package	pallet with PVC soft flim
Range of use	Garden, Lawn, Balcony, Corridor, Garage, Pool&SPA Surrounds, Boardwalk, Playground

Zhejiang Huaxiajie Macromolecule Building Material Co., Ltd., which was established in 2004, is a special manufacturer of PVC wall and Coupling Vinyl Decking Materials , PVC doors and doorframes, and plastic-wood skirting and flooring. Our products are environment friendly.
With advanced production lines from Germany and Italy, we have a total annual capacity of over 5 million square meters PVC wall and ceiling panels, over 6,000MT plastic-wood products, and over 2,000MT other PVC products.

Test Reprot:

Table 2.Test Results

Test Method

Characters

Result

ASTM G155

Weathering Resistance

After 2000hours weathering test

Grey scale:3

There was some color changer on the

surface.

Table 2

Test Method	Characters	Result
ASTM D 256	Impact resistance	59.1 J/m Break type Complete break
ASTM D 790	Flexural strength (Thickness:3mm,span:48mm)	MOR::79.8Mpa MOE:3107Mpa
ASTM D1037	Water absorption and Swelling in thickness (24hours immersion)	Water absorption:0.16% Swelling thickness:0.10%
ASTM D2395	Specific gravity	1.17g/cm3
ASTM D4060	Abrasion Resistance (CS-17,2000cycles)	Weight Loss:0.12g
ASTM D696	Coefficient of linear thermal expansion (-30℃~30℃)	5.13*10-5 1/℃
ASTM D2394	Slip Resistance Test		Static Slip Resistance	Dynamic Slip Resistance
		Dry surface	0.63	0.45
		Wet Surface	0.69	0.68
ASTM D638	Tensile strength	37.2MPa
ASTM D7032and ASTM D6109	Flexural strength:Initial (Thickness:27mm,span 432mm)	MOR:33.2Mpa MOE:2073Mpa
	Flexural strength Temperature and moisture effects(-29℃ for 7days)	MOR:35.0Mpa,increase 5.4% MOE:2209Mpa, increase 6.6%
	Flexural strength Temperature and moisture effects(52℃ for 7days)	MOR:35.2Mpa,increase 6.0% MOE:2162Mpa, increase 4.3%
	Flexural strength Temperature and moisture effects(immersing in water for 7days)	MOR:33.4Mpa,increase 0.6% MOE:2103Mpa, increase 1.4%
ASTM D7031 and ASTM D6109	Flexural strength (Thickness:27mm,span:432mm) (After freeze-thaw resistance)	MOR:33.4Mpa,increase 6.0% MOE:2167Mpa, increase 4.5%
ASTM D1761	Fastener withdrawal test	2387.8N